Wall and floor tiles were fabricated by a dry pressing method using waste glass and clay.The properties of the tiles such as absorption, bulk density, porosity, compressive strength, andabrasion loss are investigated with the firing temperature and glass content. The properties areimproved with increasing both the firing temperature and glass content. These properties, except thecompressive strength, tend to be saturated from the glass contents of 70 wt % in the case of 1050 [removed info].The compressive strength shows the maximum values at the glass contents of 70 wt% and then whichare decreased with increasing the glass contents. The optimal properties obtained in the tiles are thewater absorption of about 0.9 %, the bulk density of about 2.3 g/cm3, the apparent porosity of about2.1 %, the compressive strength of about 210 MPa, and the abrasion loss of about 0.022 g, when thecomposition containing the glass of 70 wt% is fired at 1050[removed info]. These results are better than theproperties of commercial clay tiles, due to easy melting and densification of glassy phase in the tiles
Materialart:
Digitale Medien
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/01/51/transtech_doi~10.4028%252Fwww.scientific.net%252FKEM.317-318.755.pdf
Permalink