ISSN:
1572-9605
Schlagwort(e):
Yb-123
;
melt processing
;
phase formation
;
reduced oxygen partial pressure
Quelle:
Springer Online Journal Archives 1860-2000
Thema:
Elektrotechnik, Elektronik, Nachrichtentechnik
,
Physik
Notizen:
Abstract The formation of Yb-123 has been studied at different temperatures in air and in reduced oxygen partial pressure. It is found that the stability and/or the formation kinetics of Yb-123 phase is a major hurdle in manufacturing phase-pure Yb-123 in air. However, under reduced oxygen partial pressure, Yb-123 forms rapidly and more than 90% phase-pure Yb-123 is achieved within three sintering steps. Rods made from this powder were melt-processed in air and showed a T c of 90 K. Kinetic studies performed by interrupting the growth during the directional solidification of these rods revealed a growth mechanism similar to that of Y-123 and a maximum growth rate of 7.2 mm/h for a stable planar interface. EPMA of the interface showed the liquid to be rich in barium cuprates with a Ba:Cu ratio of 1:3.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1023/A:1022670809652
Permalink