Keywords:
PACS. 61.72.Ji Point defects (vacancies, interstitials, color centers, etc.) and defect clusters - 76.30.Mi Color centers and other defects - 76.60.Cq Chemical and Knight shifts
Source:
Springer Online Journal Archives 1860-2000
Topics:
Physics
Notes:
Abstract: AlH3 powder was bombarded with energetic electrons at 20 K and at room temperature and investigated by EPR, NMR, X-ray diffractometry, and microwave dielectric-constant measurements. The EPR spectra of the irradiated powder and of a selected single crystal cuboid of mm edge show a complex asymmetric line centered at g = 2.009, with a Curie-like temperature dependence, attributed to radiation-induced color centers and/or their agglomerates. At the same time, the grains, which have become shiny black after irradiation, exhibit an increase of both the real and the imaginary part of . 27Al-NMR spectra of the irradiated powder present a Knight-shifted line at 1600(50) ppm, close to the position of bulk metallic Al, and corresponding to a concentration of c(Al) . In addition, the main hydride line differs from that before irradiation, demonstrating an alteration of environmental symmetry. The irradiation induces also a change in shape and width of the 1H-NMR line, another indication of symmetry change in the lattice. Finally, a refined X-ray single-crystal structure analysis of the irradiated cuboid indicates a change of structure from trigonal R -3 c to R -3, with a loss of mirror symmetry for the two Al sites caused by the introduction of Al-defects in the vicinity of one of them.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/s100510050266
Permalink