Diacids with variable spacer length were prepared by condensation of trimellitic anhydride and ω-amino acids. From these diacids, homopolyesters were prepared by thermal condensation with the acetates of hydroquinone or 4,4′-dihydroxy biphenyl and a series of copolyesters containing 4-hydroxy benzoic acid. The same LC poly(ester imide)s could also be prepared in a “one-pot procedure” from trimellitic anhydrid, lactams, and bisphenol acetates. The differential scanning calorimetry (DSC) traces of most poly(ester imide)s exhibit two endotherms representing the solid → LC phase transition (Tm1) and the LC phase → isotropic melt transition (Tm2). Observation under the polarizing microscope and wide-angle X-ray scattering (WAXS) measurements suggest that the LC phase formed immediately above the melting points (Tm1) have a smectic character. Poly(ester imide)s of 4,4′-dihydroxybiphenyl possess higher melting points and a broader temperature range of the LC phase than those of hydroquinone. The copolyesters possess a nematic melt over a broad temperature range. Thermomechanical analyses under low pressure (0.05 kg/mm2) gave heat distortion temperatures close to the melting points (Tm1), and under high pressure (1 kg/mm2), values between Tm1 and the glass transition temperatures (Tg). Thermogravimetric measurements indicate that processing from the melt is feasible up to temperatures around 340°C.
Zusätzliches Material:
7 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/pola.1989.080270204
Permalink