There is a good adhesion between terpolymers containing ethylene, propylene, and ethylidenenorbornene and galvanically deposited metal after the pretreatment with chromic acid. The peel strength depends on the size and distribution of the sequence lengths and increases with increasing density. Only few carbonylic groups are detectable by the help of spectroscopic methods so that the part of chemical adhesion is negligible. Therefore the main part of the adhesion consists in the physical bondings between metal and polymer.After the ozonisation of the polymers the peel strength is not very high. Its average value is about 5 N/25 mm. The chemical changes are observed by spectroscopic methods. The number of functional groups at the surface of the polymers seems to be very low.
Notes:
Durch Vorbehandlung von Terpolymeren aus Ethylen, Propylen und Ethylidennorbornen mit Chromschwefelsäure kann eine gute Haftung galvanisch aufgebrachter Metallschichten erreicht werden. Die Abzugsfestigkeit hängt von der Größe und Verteilung der Sequenzlängen ab und erhöht sich mit steigender Dichte des Polymeren. Die spektroskopisch nachweisbare Konzentration and Carbonylgruppen ist gering, demzufolge auch ihr Anteil an der Haftung. Hier überwiegt der Anteil der physikalischen Haftung zwischen Metall und Polymerem.Die Ozonisierung der Polymeren führt zu keiner hohen Abzugsfestigkeit. Sie liegt im Mittel bei 5 N/25 mm. Die durch die Reaktion hervorgerufenen chemischen Veränderungen des Polymeren können spektroskopisch verfolgt werden. Die Anzahl funktioneller Gruppen an der Polymeroberfläche ist wahrscheinlich schr gering.
Additional Material:
8 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/apmc.1983.051150112
Permalink