high impact polystyrene
;
polychromatic irradiation
;
viscosity
;
tensile impact
;
yellowing
;
Chemistry
;
Polymer and Materials Science
Quelle:
Wiley InterScience Backfile Collection 1832-2000
Thema:
Chemie und Pharmazie
,
Maschinenbau
,
Physik
Notizen:
Different grades of impact-modified polystyrene were studied by viscometry, tensile impact test and colour change upon exposure to polychromatic irradiation at 55°C in air. The samples underwent extensive reduction in intrinsic viscosity [η] and tensile impact strength, and yellowed upon polychromatic irradiation (λ ≥ 290 nm). Chain-scission during photo-oxidative degradation was also studied under conditions where evolution of volatiles was negligible. Tristimulus values were calculated for unirradiated and irradiated samples. The rate of oxidative degradation was maximum in the sample possessing higher unsaturation content.
Zusätzliches Material:
5 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/pi.1995.210360402
Permalink