Description / Table of Contents:
Crystal Growth and Structure Determination of BaPb(1-x)BixO3 (x = 0.15)Single crystals (0.15X0.20X0.20 mm) of BaPb(1-x)BixO3 (x = 0.15) have been grown from a lead (II)-oxide melt. The refinement of the crystal structure (I4/mcm; a = 6.047(5), c = 8.603(8) Å; Z = 4; 281 diffractometer data, R = 0.03) resulted in Pb(Bi)—O—Pb(Bi) bonding angles of 180° (2X), and 165° (4X) within the a/b plane. The identity of single crystals and powder material was ensured by an Rietveld profile fit of the X-ray powder diagram. The compositions of the single crystals have been determined applying electron microprobe techniques. Tc of the single crystals was found to be 13.2 K (onset, S QUID-magnetometer).
Notes:
Von BaPb(1-x)BixO3(x = 0,15) wurden Einkristalle (0,15X0,20X0,20mm) für die Röntgenstrukturanalyse aus einer Blei(II)-oxid-reichen Schmelze gezogen. Die Verfeinerung der Kristallstruktur (I4/mcm; a = 6,047(5), c = 8,603(8) Å; Z = 4; 281 Diffraktometerdaten; R = 0,03) ergab Klarheit über die Pb(Bi)—O—Pb(Bi)-Winkel: 180° (2X) und 165° (4X) in der a/b-Ebene. Die Übereinstimmung zwischen Einkristall und Pulvermaterial wurde durch eine Profilanpassung des Pulverdiagramms nach Rietveld sichergestellt, die Zusammensetzung der Einkristalle bezüglich der Metallverhältnisse mit Hilfe der energiedispersiven Analyse (EDX) bestimmt. Die Sprungtemperatur der Einkristalle wurde mit Hilfe eines S QUID-Magnetometers zu 13,2 K („onset“) ermittelt.
Additional Material:
3 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19915930119
Permalink