Observations in connection with the atmospheric corrosion of hot-dip galvanized surfacesA report on tests having been carried on since 1963 in an industrial atmosphere, with 2 specimens being examined every 6 months. Formation of rust starts after about 30 months, proceeding from the edge of the specimen; after 54 to 60 months the top surface of the specimen has become covered with rust areas, there is a typical difference between the corrosion losses on the upper and lower face of specimen (3:1 by weight). Hard zinc and pure zinc practically show identical behaviour. Hard zinc experience an initial increase in weight, while pure zinc is loosing weight from the very beginning; after this initial period, however, the weight loss curves are parallel.
Notes:
Seit 1963 laufende Versuche in Industrieatmosphäre mit Prüfung von jeweils zwei Proben im Abstand von 6 Monaten. Die Rostbildung beginnt nach etwa 30 Monaten, ausgehend vom Rand der Probe, und nach 54 bis 60 Monaten sind die Oberseiten der Proben mit Rostflächen bedeckt. Charakteristisch sind die Unterschiede im Korrosionsverlust auf Ober- und Unterseite der Probe (gewichtsmäßig etwa 3:1). Hartzink- und Reinzinkoberflächen verhalten sich praktisch analog. Im Falle von Hartzink ist zu Beginn eine Gewichtszunahme festzustellen, während bei Reinzink sofort Gewichtsverlust auftritt; danach verlaufen die Gewichtsverlustkurven parallel.
Additional Material:
7 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19700210404
Permalink