ISSN:
0887-6266
Schlagwort(e):
poly(p-phenylene sulfide) fiber
;
zone-drawing
;
zone-annealing
;
mechanical properties
;
DSC thermogram
;
viscoelastic properties
;
Physics
;
Polymer and Materials Science
Quelle:
Wiley InterScience Backfile Collection 1832-2000
Thema:
Chemie und Pharmazie
,
Physik
Notizen:
A zone-drawing and zone-annealing treatment was applied to poly(p-phenylene sulfide) fibers in order to improve their mechanical properties. The zone-drawing (ZD) was carried out at a drawing temperature of 90°C under an applied tension of 5.5 MPa, and the zone-annealing (ZA) was carried out at an annealing temperature of 220°C under 138.0 MPa. The differential scanning calorimetry (DSC) thermogram of the ZD fiber had a broad exothermic transition (Tc = 110°C) attributed to cold-crystallization and a melting endotherm peaking at 286°C. The Tc of the ZD fiber was lower than that (Tc = 128°C) of the undrawn fiber. In the temperature dependence of storage modulus (E′) for the ZD fiber, the E′ values decreased with increasing temperature, but increased slightly in the temperature range of 90-100°C, and decreased again. The slight increase in E′ was attributable to the additional increase in the crosslink density of the network, which was caused by strain-induced crystallization during measurement. The resulting ZA fiber had a draw ratio of 6.0, a degree of crystallinity of 38%, a tensile modulus of 8 GPa, and a tensile strength of 0.7 GPa. © 1998 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 36: 1731-1738, 1998
Zusätzliches Material:
10 Ill.
Materialart:
Digitale Medien
Permalink