cobalt-chromium alloys
;
oxidation sulfidation
;
conjoint attack
Quelle:
Springer Online Journal Archives 1860-2000
Thema:
Maschinenbau
Notizen:
Abstract Cobalt alloys containing up to 25% chromium have been exposed to Ar-10% SO2 atmospheres at temperatures between 600 and 1000° C. The results show that, although an increase in chromium content leads to a reduction in the reaction rate, even to negligible rates in the cases of the higher chromium contents, all of the alloys are eventually subjected to rapid attack at more or less longer times, depending on the chromium content. The mechanism of the reaction appears to involve the formation of a more or less protective oxide layer which is eventually penetrated by sulfur. The sulfur forms chromium sulfides at the metal-scale interface, removing the chromium from solution and causing an expansion that cracks the protective scale, allowing both the ingress of gas and the formation of rapidly growing cobalt compounds. The process occurs rapidly with Co-5% Cr alloys, whereas, only the initial sulfur penetration is observed with Co-25% Cr alloys during the time scale of the investigation. The penetration of sulfur is thought to occur as a molecular gas species permeating through the scale down physical defects.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1007/BF00605110
Permalink