Knowledge about stress corrosion cracking and corrosion fatigue until 1970; specific aggressive media to cause stress corrosion cracking: alkali solution, nitrates, ammonia salts - meaning of the constant strain rate technique and stress corrosion cracking in bicarbonate solutions - dependence of tensile stress, strain and strain rate upon time; significance of strain rate - investigations in bicarbonate, carbonate and hydroxide solutions - critical potential ranges - relation between strain rate and low cycle fatigue - theoretical differences between stress corrosion cracking and corrosion fatigue in spite of gradual transient in physical appearances.
Notizen:
Stand des Wissens über Spannungsriß- und Schwingungsrißkorrosion bis um 1970; spezifische Medien für Spannungsrißkorrosion: Alkalilauge, Nitrate, Ammoniumsalze - Bedeutung der constant-strain-rate-Technik und Bikarbonat-Spannungsrißkorrosion - Zeitabhängigkeit von Zugspannung, Dehnung und Dehngeschwindigkeit; Bedeutung der Dehngeschwindigkeit - Untersuchungen in Bikarbonat-, Karbonat- und Hydroxidlösungen - kritische Potentialbereiche - Zusammenhang zwischen Dehngeschwindigkeit und langsamer Ermüdung - theoretischer Unterschied zwischen Spannungsrißkorrosion und Korrosionsermüdung trotz phänomenologisch gleitender Übergänge.
Zusätzliches Material:
28 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/mawe.19780090106
Permalink