Description / Table of Contents:
A method for polymerization of vinylchloride (VC) at atmospheric pressure is described, in which the gaseous monomer is polymerized with K2S2O8 as an initiator at 45°C to 60°C. The amount of the polymer formed (so-called U-PVC) as a function of the reaction time depends on the rate of monomer flow. The reaction rate increases with higher initiator concentration as well as with increasing temperature. It is also possible to initiate the polymerization with the redox-system K2S2O8/Na2SO3/Cu2+ within the range of 0°C to 20°C.By means of transmission electronmicroscopic (TEM) investigations the particle size and particle size distribution as a function of polymerization time and temperature was determined.
Notes:
Es wird die Polymerisation von gasförmigem Vinylchlorid (VC) im Temperaturbereich von 45°C bis 60°C mit Kaliumperoxodisulfat als Initiator bei Atmosphärendruck beschrieben. Die Menge des gebildeten Polymeren (sog. U-PVC) im Verhältnis zur Reaktionsdauer hängt vom Monomerdurchsatz ab.Die Polymerisationsgeschwindigkeit kann sowohl durch Erhöhung der Initiatorkonzentration als auch der Temperatur gesteigert werden. Mit dem Redoxsystem K2S2O8/Na2SO3/Cu2+ ist es möglich, bei sonst konstanten Bedingungen im Temperaturbereich von 0°C bis 20°C zu polymerisieren.Mittels transmissionselektronenmikroskopischer (TEM) Untersuchungen wurde die Größe und die Größenverteilung der Teilchen in Abhängigkeit von der Polymerisationszeit und Temperatur ermittelt.
Additional Material:
8 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/apmc.1983.051130110