The melting points of liquid-crystalline main chain polyesters made from hydroquinone derivatives and substituted terephthalic acids can be lowered strongly by attaching flexible side chains or voluminous side groups. The solid state of poly(2′-phenyl-1′,4′-phenylene-2,5-dihexyloxyterephthalate) is even amorphous with a glass transition at 47°C and a phase transition to isotropic melt at 184°C. Beside the low phase transition temperatures, this polyester is readily soluble in toluene and tetrahydrofuran. Up to 40 mol-% of 2,5-dihexyloxyterephthalic acid may be replaced by unsubstituted terephthalic acid without a strong influence on the phase transition temperatures and the solubility of the polyester. The E-modulus of the copolyester with 40 mol-% of terephthalic acid reaches 7700 MPa.
Notes:
Bei flüssigkristallinen Hauptkettenpolyestern aus Hydrochinon- und Terephthalsäurederivaten lassen sich die Schmelztemperaturen durch “Anheften” von flexiblen Seitenketten und raumfüllenden Gruppen stark absenken. Poly(2′-phenyl-1′,4′-phenylen-2,5-dihexyloxyterephthalat) liegt im festen Zustand sogar amorph vor; die Glasübergangstemperatur beträgt 47°C, der Phasenübergang zur isotropen Schmelze erfolgt bei 184°C. Neben tiefen Phasenübergangstemperaturen zeichnet sich dieser Polyester durch eine gute Löslichkeit in Toluol und THF aus. Bis zu 40 mol-% der 2,5-Dihexyloxyterephthalsäre lassen sich durch unsubstituierte Terephthalsäure ersetzen, ohne die Phasenübergangstemperaturen und die Löslichkeit des Polyesters wesentlich zu beeinflussen. Der Copolyester mit 40 mol-% Terephthalsäure zeigt im Zugversuch nach DIN 53455 einen E-Modul von 7700 MPa.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/apmc.1995.052240119