The influence of 90 MeV 16O ion irradiation on the electric and magnetic properties of epitaxial thin films of La0.75Ca0.25MnO3 is studied. These films were deposited on LaAlO3(100) substrates by the pulsed excimer laser deposition technique. The thickness of each film was about 3000 Å. The high quality of the films was ensured by x-ray diffraction and transport measurements. The films were irradiated with 90 MeV oxygen ions at different doses (1011–1014 ions/cm2). It is observed that at a low dose of 1011 ions/cm2 the resistivity peak temperature (Tp) and the Curie temperature (Tc) increase, however as the dose is increased further, the Tp and Tc decrease. At the higher dose of 1014 ions/cm2, the film becomes insulating and does not show any peak in the resistivity–temperature curve down to 60 K. These results are discussed in terms of the effects of ion induced compositional inhomogeneity and strain on the film properties. © 1998 American Institute of Physics.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1063/1.367792