Torsional cycling of cold pressure welded zirconium/steel-specimens. Low-cycle fatigue of cold pressure welder zirconium/steel-specimens has been studied in cyclic torsion. The critical number of cycles Ncr instead of the number of cycles to final failure Nf is taken for evaluation of the endurance life in low-cycle fatigue. Ncr is defined as the number of cycles leading to the formation of a crack which noticeably weakens the specimen. The relationship NKra · Δγ = const. is achieved for bonded specimens. The results have been correlated with the observations in unwelded zirconium and steel to predict the endurance life of bonded specimens. Microstructure studies revealed crack initiation at points of intense slip in zirconium. Fracture occured always in zirconium outside the welded zone.
Notizen:
Plastoermüdung (low-cycle fatigue) an kaltpreßgeschweißten Zirkonium/Stahl-Proben wurde im Torsionswechselversuch untersucht. Zur Bestimmung der Lebensdauer bei Plastoermüdung wurde die kritische Lastspielzahl NKr anstelle der Bruchlastspielzahl NB verwendet. NKr ist die Lastspielzahl, bei der Risse auftreten, die die Probe merklich schwächen. Der Zusammenhang NKra. Δγ = C wurde auch für geschweißte Proben gewonnen. Die Ergebnisse wurden mit den Beobachtungen an ungeschweißten Proben in Zusammenhang gebracht, um die Lebensdauer der geschweißten Proben voraussagen zu können. Mikroskopische Untersuchungen zeigten die Anrißbildung an Stellen intensiver Gleitung in Zirkonium. Der Bruch erfolgte immer außerhalb der Schweißnaht im Zirkonium.
Zusätzliches Material:
9 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/mawe.19740050205