Contribution to the long time behaviour of the steel X 10 NiCrAlTi 32 20 at high temperaturesAt the instance of the working community for high temperature materials an evaluation of the available results of creep tests on the steel X 10 NiCrAlTi 32 20 (Incoloy 800) was carried out. Test values of nine melts with 0.03 to 0.07% C and 0.49 to 0.93% (Al + Ti), examined in the solution treated condition in the temperature range from 600 to 1000 °C, could be evaluated. The influence of carbon and (Al + Ti) content and of the grain size on the creep values is discussed. The ductility behaviour in the creep rupture tests is also treated. In this connection results of tensile tests on smooth and notched specimens of two melts with 0.07 and 0.02% C after annealing up to 104 h at 550 and 600 °C under service stresses are reported.
Notizen:
Im Auftrage der Arbeitsgemeinschaft für Hochtemperaturwerkstoffe wurde eine Auswertung der verfügbaren Ergebnisse aus Zeitstandversuchen an dem Stahl X 10 NiCrAlTi 32 20 durchgeführt. Hierbei konnten Versuchsunterlagen von 9 Schmelzen mit 0,03 bis 0,07% C und 0,49 bis 0,93% (Al + Ti), die im lösungsgeglühten Zustand im Temperaturbereich von 600 bis 1000 °C geprüft wurden, ausgewertet werden. Der Einfluß der Gehalte an Kohlenstoff und (Al + Ti) sowie der Korngröße auf die Zeitstandwerte wird erörtert.Das Zähigkeitsverhalten bei den Zeitstandbruchversuchen wird ebenfalls behandelt. Im Zusammenhang damit wird über Zugversuche an glatten und gekerbten Proben von zwei Schmelzen mit 0,07 und 0,02% C nach bis zu 104stündigem Glühen bei 550 und 600 °C unter Betriebsspannungen berichtet.
Zusätzliches Material:
24 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/mawe.19800110507