Description / Table of Contents:
Problem of intercrystalline corrosion susceptibility of an inadequately stabilized steel 1Cr18Ni9TiA study of the relations between carbide precipitation and the corrosion susceptibility has revealed that the steel under study (0.11 % C, 0.42 % Ti) after dissolution treatment is comparable to a non-stabilized steel containing about 0.06% C. Increasing the carbon content gives rise to an ultimate displacement of the sensitivity range to extended durations and lower temperatures of the thermal treatment. From a practical point of view it is, however, permissible to consider thickness without giving rise to the danger of intercrystalline corrosion in moderate oxidants.
Notes:
Die Untersuchung der Beziehungen zwischen der Carbidausscheidung und der Korrosionsanfälligkeit hat gezeigt, daß der untersuchte Stahl (0,11 % C,0,42 % ti) nach Lösungsglühen sich wie ein nicht stabilisierter Stahl mit etwa 0,06 % C verhält. Die Erhöhung des Gehalts an gebundenem Kohlenstoff führt zu einer weiteren Verschiebung des Anfälligkeitsbereiches nach längeren Zeiten und niedrigeren Temperaturen der Wärmebehandlung. Von der Praxis her kann jedoch dieser Stahl als bis zu einer gewissen Dicke schweißbar angesehen werden, ohne daß es in Gegenwart von mäßig starken Oxidationsmitteln zu interkristaliner Korrosion kommt.
Additional Material:
21 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19740250506