Influence of HCl and Cl2 on high temperature corrosion of 2 1/4Cr 1 Mo Steel in atmospheres with high oxygen pressuresThe oxidation of the 2 1/4 Cr 1 Mo steel was investigated at 773 K in oxidizing He-O2-HCl atmospheres. The addition of HCl to He-O2 atmospheres leads to accelerated oxidation rates. Below porous and cracked oxide scales condensed chlorides are formed. At low HCl pressures 0-1000 vppm the “active oxidation” is determining the corrosion process; i.e. oxidation of evaporating chlorides within the oxide scale. For higher HCl contents 1000-3000 vppm the corrosion behaviour changes to paralinear; i.e. simultaneous parabolic oxide growth and linear mass loss by chloride evaporation.
Notes:
Die Oxidation des 2 1/4Cr1Mo-Stahls in oxidierenden He-O2-HCl-Atmosphären bei 773 K wurde untersucht. Der Zusatz von HCl zu He-O2-Atmosphären führt zu stark beschleunigter Oxidation. Unter porösen und rissigen Oxidschichten bilden sich feste Chloride. Bei niedrigen HCl-Drücken 0-1000 vppm bestimmt „aktive Oxidation“ den Korrosionsprozeß; d.h. Oxidation flüchtiger Chloride innerhalb der Oxidschicht. Bei höheren HCl-Drücken 1000-3000 vppm erfolgt ein Übergang zum paralinearen Korrosionsverhalten, d.h. gleichzeitiges parabolisches Oxidwachstum und lineare Massenabnahme durch das Abdampfen von Chloriden.
Additional Material:
4 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19900410602