Studies on Oxide Catalysts. XXV. Catalytic Activity and Aging Properties of Modified Mordenites in the Cracking of n-OctaneMeH-mordenites (Me = Li, K, Mg, Ca, Ba) were prepared by ion exchange starting with H-mordenite (SiO2/Al2O3 mole ratio = 14). To characterize these samples the cracking of n-octane was used as catalytic test reaction. Surface OH groups and the adsorption of NH3 on these samples were investigated by i. r. spectroscopy. Unaffected by the kind of the exchanged cation the Brönsted acidity of the H-mordenite decreases monotonously with increasing content of the incorporated cation. The catalytic activity and (to a much higher degree) the rate of deactivation by coking during the reaction decrease as the Brönsted acidity decreases. The strong dependence of the Brönsted acidity on the deactivation rate points to a multi-site mechanism of the coking process.
Notes:
MeH-Mordenite (Me = Li, K, Mg, Ca, Ba) wurden ausgehend von einem H-Mordenit (Molverhältnis SiO2/Al2O3 = 14) durch Ionenaustausch hergestellt. Als Testreaktion zur Katalytischen Charakterisierung diente die n-Octanspaltung. IR-spektroskopisch wurden die OH-Oberflächengruppen und die Adsorption von NH3 an den Proben untersucht. Unabhängig von der Art des eingetauschten Kations sinkt die Brönsted-Acidität des H-Mordenits monoton mit steigendem Gehalt an den eingetauschten Kationen. Die katalytische Aktivität und (im weit Stärkeren Maße) die Desaktivierungsgeschwindigkeit (infolge „Verkokens“ während der Reaktion) sinken symbat mit der Brönsted-Acidität. Die starke Abhängigkeit der Geschwindigkeit der Desaktivierung von der Brönsted-Acidität weist auf einen Mehrzentrenmechanismus für die Verkokung hin.
Additional Material:
5 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19784450107