Samples of polyvinylchlorid mixed with a fine granulated aluminium as filler were investigated. The specific electric resistance was measured in a temperature interval from 293 to 373 K and the activation energy as a function of aluminium concentration was calculated.The thickness of the dielectric layer absorbed on the surface of the metal particles and the static volt-ampere characteristics were measured at different temperatures. They show s-type switching and hysteresis.Suggestions are made about possible mechanisms of conductivity.
Notes:
Es wurde Polyvinylchlorid mit Aluminiumpulver als Füllstoff untersucht. Es wurde der spezifische elektrische Volumenwiderstand im Temperaturbereich von 293-373 K bestimmt und die Aktivierungsenergie als Funktion der Konzentration des Metallfüllstoffs berechnet.Es wurde die Dicke der dielektrischen Schicht, die auf den Metallteilchen adsobiert ist, bestimmt und die Feldstärke berechnet, bei der das System vom hochohmigen in den niederohmigen Zustand umschaltet. Im niederohmigen Zustand wurden die stati schen Strom-Spannungskennlinien bei verschiedenen Temperaturen aufgenommen. Es wurde eine S-Typ Kurve bei der Umschaltung in den niederohmigen Zustand und eine Hysteresis beobachtet.Es werden einige allgemeine theoretische Betrachtungen über die vorliegenden Mechanismen der Leitfähigkeit gegeben.
Additional Material:
4 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/apmc.1984.051210102