Description / Table of Contents:
Homopolymers of 3(resp. 5)-vinyl-pyrazolderivates were obtained by radical solution polymerisation and their properties were examined. Resins of limited swelling were prepared by copolymerisation of 2.5 mole-% bis-[3(resp. 5)-vinyl-5(resp. 3)-pyrazolyl]-ketone with 3(resp. 5)-vinyl-5(resp. 3)-pyrazolecarboxylic acid ethyl ester (I) or 3(resp. 5)-vinyl-4.5(resp. 3)-pyrazoledicarboxylic acid dimethyl ester (II). By saponification they were converted to poly-vinyl-pyrazole-carboxylic acid resins (resin A1 and resin A2). The latter are chelating resins of high capacity. The possibility of binding the metal ions Cu2⊕, Ni2⊕, Zn2⊕, and Mg2⊕ and the sorption rate was studied in the pH range 1-5.5.
Notes:
Durch radikalische Lösungspolymerisation wurden Homopolymere von 3(bzw. 5)-Vinylpyrazol-derivaten erhalten und deren Eigenschaften untersucht. Durch Copolymerisation von 2,5 Mol-% Bis-[3(bzw. 5)-vinyl-5(bzw. 3)-pyrazolyl]-keton mit 3(bzw. 5)-Vinyl-5(bzw. 3)-pyrazol-carbonsäureäthylester (I) bzw. 3(bzw. 5)-Vinyl-4.5(bzw.3)-pyrazol-dicarbonsäuredimethylester (II) wurden Harze dargestellt, die nur begrenzt quellbar sind und die durch Verseifung in Poly-[vinyl-pyrazol-carbonsäure]-harze (Harz A1 und Harz A2) überführt wurden. Diese Harze stellen hochkapazitive Chelatharze dar. Es wurde das Metallionenbindungsvermögen für Cu2⊕, Ni2⊕, Zn2⊕ und Mg2⊕ und die Aufnahmegeschwindigkeit in Abhängigkeit vom pH-Wert im Bereich von pH 1 bis pH 5,5 untersucht.
Additional Material:
3 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/macp.1971.021500102