Nd8Fe73Co5Hf2B12 alloys were cast as strips (thick continuous ribbons with thickness t=100–160 μm) by a chill disk melt spinning technique (vdisk=3 m/s) from a master alloy prepared by arc melting (A) and from two prealloyed components (B). Samples obtained by the B procedure revealed in the as-cast state, good magnetic properties with an unusually high value of the coercivity, Hc=10.3 kOe, for the substoichiometric Nd2Fe14B system. A high degree of structural refinement and a homogeneous dispersion of the phases are attained in sample B. The strength and type of magnetic interactions between the grains are presented by δM and irreversible susceptibility plots. © 2000 American Institute of Physics.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1063/1.373340
| Library |
Location |
Call Number |
Volume/Issue/Year |
Availability |