The magnetic and crystalline properties of a plasma-sprayed coating of the microwave absorbing zinc-nickel ferrite, (Zn0.41Ni0.59 )Fe2O4 have been studied at 300 K using the Mössbauer effect and x-ray diffraction (XRD). Both techniques indicate that the plasma-sprayed material separated into two phases. The first is a nickel-rich phase with magnetic fields of 47.5 and 44.5 T at the tetrahedral and octahedral sites, respectively. The second is a zinc-rich phase, zinc meta-ferrite, having a small magnetic field of 4.2 T. The quadrupole splitting of this second phase is ΔE=0.34 mm s−1, which is the same as in pure nonmagnetic zinc ferrite. XRD analysis shows that the zinc-rich phase remains cubic with a0= 8.389 A(ring) and the zinc meta-ferrite phase is tetragonal with the same lattice parameters as the cubic phase except for one elongated axis given by c0 =8.488 A(ring). This is much larger than the spacing for any of the series of zinc-nickel ferrites. The isomer shift of the zinc meta-ferrite is 0.710 mm s−1, which indicates that a large fraction of Fe3+ was reduced during the spraying process. Annealing the sprayed coating at temperatures less than 400 °C converted the zinc meta-ferrite into a magnetic phase that now exhibits magnetic fields close to those in the nickel-rich phase. However, the large isomer shift remains, indicating that the ferrous iron is still present. XRD shows that the phase is now cubic. Annealing up to 650 °C gradually oxidized all of the Fe2+ in the material and restored the magnetic and crystalline properties of the plasma-sprayed coating to very close to those of the unsprayed ferrite.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1063/1.348027