Mechanically alloyed Al65Cu20Ti15 amorphous alloy powder with 10 wt.% nano-TiO2dispersion was consolidated by high pressure sintering (HPS) at room temperature and/or 300-450oC for about 1 min using a uniaxial pressure of 8GPa. The sintered material was examined byXRD and TEM. Excellent hardness and strength were obtained in selected sintered samples of 8.34GPa and 1600 MPa respectively, although ductility was very low (〈 1%)