A method is introduced to prepare almost-spherical submicrometer-sized α-alumina via surface modification of γ-alumina with an alumina sol. Milled γ-alumina, in the presence of 3 wt% of α-alumina with a median particle size (d50) of 0.32 μm (AKP-30), produced irregularly shaped α-alumina with d50∼0.3 μm after heat treatment at 1100°C for 1 h. γ-alumina that had been surface-modified by milling in the presence of 3 wt% of the alumina sol resulted in almost-monosized, spherical α-alumina ∼0.3 μm in size after heat treatment at 1100°C for 1 h. Furthermore, almost-spherical α-alumina 0.1—0.2 μm in size was obtained by milling γ-alumina with 3 wt% of AKP-30 alumina in the presence of 3 wt% of the alumina sol, followed by heat treatment at 1100°C for 1 h. The alumina sol that has been introduced in this work seems to act as a dispersant, in addition to helping to form a spherical shape.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1111/j.1151-2916.2000.tb01269.x