American Institute of Physics (AIP)
Journal of Applied Physics
74 (1993), S. 5672-5678
ISSN:
1089-7550
Quelle:
AIP Digital Archive
Thema:
Physik
Notizen:
Ultraviolet induced chemical vapor deposition was used to deposit silicon dioxide dielectrics on III–V materials at low temperature. Auger electron spectroscopy and nuclear reaction analysis measurements show that the nitrogen concentration in the layers decreases continuously with the total pressure. These results are in complete agreement with infrared transmission spectroscopic and ellipsometric measurements. The number and the nature of the paramagnetic defects measured by electron spin resonance are also shown to be dependent upon the deposition pressure. Bridging nitrogen (O3≡Si–N–Si≡O3) and oxygen-like-vacancy centers (E'1) defects are observed in small quantities (≈1016 cm−3), while overcoordinated N defects are observed in concentrations up to 1018 cm−3, depending upon deposition pressure. Such SiO2 films were used in the processing of metal-insulator InP structures. Improvement of the electrical properties also occurs when the total pressure is increased, in agreement with expectations founded on the electron spin resonance results.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1063/1.354182
Permalink
Bibliothek |
Standort |
Signatur |
Band/Heft/Jahr |
Verfügbarkeit |