In situ resistance versus temperature or time for reactions between 32 and 57.5 nm of titanium and undoped or doped polycrystalline silicon (boron, arsenic, or phosphorus, 7.9×1019–3.0×1020/cm3) has been measured and no clear correlation was found between the activation energy for the formation of the industrially important low-resistance C54-TiSi2 phase and its formation temperature. It is also demonstrated that with certain moderate doping levels typical of complementary metal-oxide-semiconductor manufacturing, boron or phosphorus-doped polycrystalline silicon can delay the formation of C54-TiSi2 more than arsenic-doped polycrystalline silicon. Finally, by using in situ resistance measurements, it is demonstrated that the "two-step'' thermal annealing process similar to a salicide process requires less thermal annealing time at high temperatures to form C54-TiSi2 than a single "one-step'' thermal anneal at the same temperature. © 1994 American Institute of Physics.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1063/1.357897
Permalink