The acoustic emission behavior during tensile loading of two common epoxy systems of different ductility was investigated at different loading rates. At low threshold voltage, it was possible to register acoustic emissions before the final failure. Only very few emissions were recorded compared with the amount commonly recorded for metals and composite materials. The acoustic emissions detected were of burst-type, revealing a brittle damage accumulation process. They originated from the initiation and incremental growth of microcracks of stochastic nature. The events occurred before gross yielding and during the final “brittle” failure process. Basically no events were detected between gross yielding and the final failure during which large scale yielding, necking, and stable crack growth took place. The occurrence of events at the different loading rates was strongly influenced by the yielding behavior and fracture toughness, characterized by the yield stress σy and the plane-strain fracture toughness KIc respectively. KIc was inversely dependent on the total number of events up to gross yielding. The event distribution normalized with respect to the conditions at gross yielding was hardly affected by the loading rate.
Zusätzliches Material:
13 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/pen.760290805
Permalink