Studies were made of the thermal softening and degradation behavior in air of low- and high-density polyethylene (PE) grafted with acrylonitrile (AN) by electron beam prior irradiation in nitrogen. It was found that both LDPE and HDPE were made to exhibit higher softening points by grafting and that this tendency increased with increasing percent graft. The starting temperatures of the thermal degradation and thermogravimetric curves were also found to shift to higher temperatures. On the other hand, in marked contrast to the thermal softening and degradation behavior of grafted PE in air, its behavior in nitrogen showed substantial dependance on oxidative degradation, suggesting that the oxidation of PE was inhibited by polyacrylonitrile (PAN), which forms graft chains. It was considered that the oxidation-inhibiting mechanism of PAN produced in the amorphous regions prevents oxygen from dissolving and diffusing into the amorphous phase, thus inhibiting the oxidative degradation of PE, and that, when heated, PAN undergoes nitrile oligomerization and the nitrile oligomer end radicals act to trap those radicals which participate in PE oxidative degradation.
Additional Material:
10 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/app.1991.070430201
Permalink