A calcium magnesium aluminosilicate-based glass that contained 10 wt% of silicon carbide whiskers (SiCw) as reinforcement was prepared by tape casting, followed by sintering either in a conventional furnace or in a microwave oven. The results were consistent with retardation of glass sintering through whisker bridging. The glass, by itself, was sintered to almost-full density at 750°C for 4 h by conventional furnace sintering; the best sintered composite, with an estimated density of ∼90%, was obtained at 800°C with a dwell time of 4 h. Sintering at a temperature of 〉800°C did not improve the densification but rather resulted in severe whisker oxidation. A reduced densification rate was observed for the samples that were sintered in nitrogen. By contrast, in the microwave oven, almost-full density for the glass and ∼95% of the theoretical density for the composite were obtainable at 850°C for 15 min, which represented a reduction of ∼10 h of the total processing time and a reduced SiCw oxidation.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1111/j.1151-2916.1997.tb03261.x
Permalink