The Ti-Cr systems are known to consist of BCC solid solution, C36, C14, C15 Laves phase at high temperature. Among others, BCC solid solution phase has been reported to have a high hydrogen storage capacity. However, activation, wide range of hysteresis at hydrogenation/dehydrogenation, and degradation of hydrogen capacity due to hydriding/dehydriding cycles have to be improved for its application. In this study, for improving such a problem, we added on Nb. To obtain a target materials, Ti-1Nb-10Cr, Ti-3Nb-10Cr and Ti-5Nb-10Cr specimens wereprepared by planetary ball mill. The milling process was carried out under nitrogen atmosphere. Specimens synthesized were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and thermo gravimetric analysis/differential scanning calorimetry(TG/DSC). In order to examine hydrogen absorptionkinetics, Sievert's type automatic pressure-composition- isotherm (PCI) was performed at 293, 323 , 373 and 423K under 1, 5MPa hydrogen atmosphere
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/12/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.510-511.534.pdf
Permalink