Scientific.Net: Materials Science & Technology / Trans Tech Publications Archiv 1984-2008
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
A 16Mb 1-transistor /1-capacitor (1T1C) FeRAM device was fabricated with lead-free Bi3.25La0.75Ti3.0O12 (BLT) capacitors. The key integration processes contain a scalable MTP (Merged Top-electrode and Plate-line) cell structure and reliable BLT ferroelectric capacitors. Ferroelectric properties of BLT films were optimized on the newly developed MTP cell structure. BLT films were coated on Pt/IrOx/Ir bottom electrode using sol-gel solutions. The composition of the optimized BLT film was about Bi3.25La0.75Ti3.0O12. The switchable polarization obtained in a 100nm-thick BLT film was about 20 µC/cm2 at the 3 V applied voltage, and the optimized BLT film showed a few fatigue losses about 10% up to 1 × 1011 cycles. The imprint properties of the BLT film were also characterized at 25℃ and 90℃ operating temperature after 125℃ data storage. The average cell signal sensing margin between data "1" and data "0" was measured to be about 900 mV, which is asufficiently large margin for device operation
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/12/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.510-511.530.pdf