Using suitable conditions of polymerisation low molecular weight PVC was prepared in CCl4 in the presence of isobutylen. The rate of thermal degradation increased as the molecular weight of the fraction decreased. The heat stability was less when dicyclohexylperoxodicarbonate was used instead of azoisobutyronitrile as an initiator. The substances with the lowest molecular weight were obtained as a colorless liquid by destillation of the polymerisation solvent at 90°C-110°C (10-4 Torr). The analysis of the products revealed the presence of structures which were not identical with those of PVC-homologues with low degree of polymerisation, but combination products of CCl4 and isobutylen.
Notes:
Unter geeigneten Polymerisationsbedingungen wurde niedermolekulares PVC in CCl4 in Gegenwart von Isobutylen hergestellt. Beim thermischen Abbau der fraktionierten, festen Anteile aus dem Polymerisationsansatz nimmt die Abbaugeschwindigkeit mit abnehmendem Molekulargewicht zu. Bei Verwendung von Dicyclohexylper-oxodicarbonat als Initiator gegenüber. Azoisobutyronitril verschlechtert sich die thermische Stabilität merklich. Die Substanzen mit dem niedrigsten Molekulargewicht wurden aus dem bei der Polymerisation verwendeten Lösungsmittel als farblose Flüsigkeit bei 90°C-110°C (10-4 Torr) destilliert. Es handelt sich hierbei jedoch nicht um PVC-Homologe mit niedrigem Polymerisationsgrad; vielmehr konnte mit spektroskopischen Methoden nachgewiesen werden, daß der Hauptanteil des erhaltenen Germisches eine Verbindung ist, die aus der Kombination von Tetrachlorkohlenstoff und Isobutylen entsteht.
Additional Material:
5 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/apmc.1980.050890111
Permalink