We describe the growth of hexagonal GaN on Si(111) by gas source molecular beam epitaxy with ammonia. The initial deposition of Al, at 1130–1190 K, resulted in a very rapid transition to a two-dimensional growth mode of AlN. The rapid transition is essential for the subsequent growth of high quality GaN and AlGaN. This procedure also resulted in complete elimination of cracking in thick (〉2 μm) GaN layers. For layers thicker than 1.5 μm, the full width at half maximum of the (0002) GaN diffraction peak was less than 14 arc sec. We show that a short period superlattice of AlGaN/GaN grown on the AlN buffer can be used to block defects propagating through GaN, resulting in good crystal and luminescence quality. At room temperature, the linewidth of the GaN exciton recombination peak was less than 40 meV, typical of the best samples grown on sapphire. © 1999 American Institute of Physics.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1063/1.124920
Permalink