Wüstite in oxide layers on low-alloy steels in water vapour - I: Wüstite formationThe oxidation and corrosion behaviour in steam of low-alloy steel tubes, which are used in boilers of electric of power stations, was investigated below and above the wüstite formation temperature. Phases, microstructure and thickness of the oxide layers were determined as a function of time and temperature. The parabolic growth constant was determined for the temperature range from 600°C to 700°C. It reflects the faster oxid layer growth caused by formation of wüstite.
Notes:
Wasserdampf-Oxidation und -Korrosion der niedrig-legierten Stähle (13 CrMo 44, 10 CrMo 9 10), die als Rohrwerkstoffe in Kraftwerkskesseln eingesetzt werden, wurden unter- und oberhalb der Wüstitbildungstemperatur (600°C) untersucht. Die Phasenzusammensetzung, das Gefüge und die Dicken der Oxidschichten wurden auf Stahlrohren in Abhängigkeit von Temperatur und Zeit ermittelt. Im Bereich von 600° bis 700°C ist infolge Wüstitbildung verstärktes Oxidschichtwachstum beobachtbar. Die parabolische Zunderkonstante wurde als Funktion der Temperatur bestimmt.
Additional Material:
6 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19880390405
Permalink