Wüstite in oxide layers on low-alloy steels in water vapour. II. Decomposition of wüstiteThe decomposition of wüstite in oxide layers on low-alloy steels formed in water steam at T 〉 600°C was investigated. The mechanism of the decomposition reaction was analysed by studying the microstructure and phase composition of differently quenched wüstite samples and of samples which had been treated at a constant temperature below 600°C. The decomposition of wüstite into the stable phases magnetite and α-iron lead to a characteristic decomposition microstructure which makes the identification of originally present wüstite clearly possible, even after the complete transformation of this wüstite into the stable phases.
Notes:
Die Zersetzung von Wüstitschichten - gebildet im Wasserdampf auf niedrig-legierten Stählen (13 CrMo 44, 10 CrMo 9 10) bei T 〉 600°C - wurde untersucht. Der Mechanismus der Zersetzungsreaktionen wurde anhand von Gefüge- und Phasenanalysen an schnell abgekühlten Proben und Proben, die einer konstanten Temperaturbehandlung bei T 〈 600°C ausgesetzt waren, ermittelt. Der Wüstitzerfall in die stabilen Phasen Magnetit und α-Eisen bei T 〈 600°C erzeugt ein charakteristisches Zersetzungsgefüge, das die eindeutige Identifizierung von ursprünglich vorhanden gewesenem Wüstit auch nach dessen vollständiger Rückumwandlung ermöglicht.
Additional Material:
6 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19880390504