ISSN:
1435-1536
Keywords:
Alkali washing
;
anionic ion exchanger
;
chemical vapor deposition nucleotide separation
;
1,3,5,7-tetramethylcyclotetrasiloxane
Source:
Springer Online Journal Archives 1860-2000
Topics:
Chemistry and Pharmacology
,
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
Abstract 1,3,5,7-Tetramethylcyclotetrasiloxane (H4) was deposited on silica gel at 80°C by utilizing a chemical vapor deposition (CVD) method, where it was catalytically polymerized to form a surface coating of polymethylsiloxane (PMS). Treated silica gel (PMS-Si) increased in weight up to a plateau level, and there was no further increase with increasing reaction time. The film of PMS was partially cross linked; typical values of crosslinking ratio and film thickness were 2% and 0.6 nm, respectively. An anionic ion exchanger containing diethylamino groups was synthesized from PMS-Si by hydrosilylation of allyl glycidyl ether followed by treatment with diethylamine. Its structure was confirmed by13C and29Si CP/MAS NMR spectroscopy and FT-IR spectrophotometry. Characterization of silica gel (DEA-Si) modified with diethylamino group was evaluated by a packing of the column for liquid chromatography. As a mixture of five nucleotides was completely separated, it was recognized that DEA-Si was operated by ion exchange action. Because the surface of the silica gel was covered with hydrophobic PMS, the peak heights and retention times did not change after washing of the column with alkaline solution.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF00657393
Permalink