polystyrene, chain scission in fracture of
;
fracture of glassy polymers, energy consuming micromechanisms
;
chain scission mechanism in fracture of polystyrene
;
glassy polymers, chain scission and fracture of
;
Chemistry
;
Polymer and Materials Science
Quelle:
Wiley InterScience Backfile Collection 1832-2000
Thema:
Chemie und Pharmazie
,
Physik
Notizen:
The number of chain scissions per unit area that occur during the fracture of partially annealed latex films from Mn ≃ 180,000 g/mol polystyrene particles of about 275 Å radius were measured and correlated to annealing times. A curve with four regimes was found. At short annealing times the curve is nearly flat, in what is called the chain pull-out regime. In the second regime, the number of chains broken per unit area increases with a 0.8 power of annealing time as entanglement of the diffusing polymer chains increases in neighboring host particles. This is in good agreement with Wool's theory which predicts a 0.75 power dependence. Then, after reaching a peak, the number of scissions decreases in the third regime, indicating a change in fracture mechanism. The number of chain scissions increases again in the fourth regime, as final healing of the film interface takes place. Fracture surface analysis reveals a rough surface for short annealing times and a smooth surface for longer annealing times. The number of polymer chain scissions per unit area of fracture surface showed no dependence on initial molecular weights for t ≫ τr where t and τr are annealing and relaxation times, respectively. The number of chain bridges crossing a unit area of interface was suggested as the basic molecular property. © 1992 John Wiley & Sons, Inc.
Zusätzliches Material:
7 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/polb.1992.090301202
Permalink