Structure of a High Temperature Modification of Calciumultraphosphate, CaP4O11, and its Crystallographic Orientation Relation with Respect to the Room Temperature PhaseThe title compound was obtained by heating a mixture of CaCO3, P4O10 in excess and H3PO4 in excess as well to 500°C and annealing for 10 days. The Calciumultraphosphate, CaP4O11, transforms at 85°C in a hot nitrogen gas stream into a second modification with orthorhombic space group (Aba2), the structure of which was determined: a = 12.683 Å, b = 12.090 Å, c = 12.627 Å, Z = 8, layer structure, R = 0.034. The crystallographic orientation relation between the two phases of CaP4O11 was determined.
Notizen:
Die Titelverbindung wurde durch Erhitzen von CaCO3 mit einem Überschuß an P4O10 und H3PO4 auf 500°C und anschließendes Tempern (10 Tage) erhalten. Das gebildete CaP4O11 wandelt sich im heißen N2-Strom bei 85°C in eine zweite CaP4O11-Modifikation um, deren Struktur bestimmt wurde: a = 12,683 Å, b = 12,090 Å, c = 12,627 Å, orthorhombische Raumgruppe Aba2, Z = 8, Schichtstruktur, R = 0,034. Die kristallographische Orientierungsbeziehung zwischen den beiden Phasen des CaP4O11 wurde ermittelt.
Zusätzliches Material:
4 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/zaac.19946200431
Permalink