ISSN:
0887-6266
Schlagwort(e):
poly(aryl ether ketone)s
;
dielectric relaxation spectroscopy
;
dynamic mechanical analysis
;
α-relaxation
;
β-relaxation
;
Physics
;
Polymer and Materials Science
Quelle:
Wiley InterScience Backfile Collection 1832-2000
Thema:
Chemie und Pharmazie
,
Physik
Notizen:
The relaxation behavior of four amorphous poly(aryl ether ketone)s was investigated using dielectric relaxation spectroscopy and dynamic mechanical analysis. The temperature dependence of the relaxation times of the glass transition process and the cooperative nature of this process were unaffected by changes in polymer structure. The temperature location of the loss peaks for all polymers progressed smoothly between the low frequency of the mechanical measurements and the higher frequencies of the dielectric probe. Differences were observed in mechanical activation energy and dielectric relaxation strength for one polymer which contained a significant concentration of meta linkages, compared with the para-linked polymers, while relaxation broadness was generally greater in the dynamic mechanical mode. Changes in chemical structure had little effect on the shape, intensity, and location of the β-relaxation peak, the main observation being that the Arrhenius activation energy measured by dynamic mechanical analysis was significantly higher than that calculated from the dielectric data. The dielectric β-relaxation was sensitive to absorbed moisture. © 1998 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 36: 851-859, 1998
Zusätzliches Material:
10 Ill.
Materialart:
Digitale Medien