The miscibility of poly(hydroxyether of bisphenol A) (phenoxy) and poly(N-vinyl pyrrolidone) (PVP) was investigated by differential scanning calorimetry (DSC) and high-resolution solid-state nuclear magnetic resonance (NMR) techniques. The DSC studies showed that the phenoxy/PVP blends have a single, composition-dependent glass transition temperature (Tg). The S-shaped Tg-composition curve of the phenoxy/PVP blends was reported, which is indicative of the strong intermolecular hydrogen-bonding interactions. To examine the miscibility of the system at molecular level, high-resolution solid-state 13C nuclear magnetic resonance (NMR) technique was employed. Upon adding phenoxy to system, the chemical shift of carbonyl carbon resonance of PVP was observed to shift downfield by 1.6 ppm in the 13C cross-polarization (CP)/magic angle spinning (MAS) together with the high-power dipolar decoupling (DD) spectra when the concentration of phenoxy is 90 wt %. The observation was responsible for the formation of intermolecular hydrogen bonding. The proton spin-lattice relaxation time T1(H) and the proton spin-lattice relaxation time in the rotating frame T1ρ(H) were measured as a function of the blend composition. The T1(H) result was in good agreement with the thermal analysis, i.e., the blends are completely homogeneous on the scale of 20 ∼ 30 nm. The six results of T1ρ(H) further indicated that the blends were homogeneous on the scale of 40 ∼ 50Å. © 1998 John Wiley & Sons, Inc. J. Polym. Sci. B Polym. Phys. 36: 2291-2300, 1998
Additional Material:
8 Ill.
Type of Medium:
Electronic Resource