ISSN:
0887-6266
Keywords:
polyethylene
;
poly(butylene terephthalate)
;
blend
;
rheology
;
Palierne's model
;
morphology
;
differential scanning calorimetry
;
crystallization
;
Physics
;
Polymer and Materials Science
Source:
Wiley InterScience Backfile Collection 1832-2000
Topics:
Chemistry and Pharmacology
,
Physics
Notes:
Crystallization at high supercooling of polybutylene terephthalate (PBT) droplets dispersed in a molten polyethylene (PE) matrix was investigated through rheological and DSC experiments. The Palierne's emulsion model was used as a theoretical framework for studying the viscoelastic behavior of the blends in different ranges of temperature: on the one hand, when the two polymers are molten (T 〉 225°C) and on the other hand, when PBT droplets are at high supercooling in the molten PE matrix (130°C 〈 T 〈 205°C). From rheological experimental evidences it was shown that molten and solidified droplets coexist at high supercooling. The Palierne's model was then successfully adapted to take into account the three phases (molten PE, molten PBT droplets, and solidified PBT droplets). The evolution of the behavior with the temperature is consistent with the growing amount of crystallized droplets. Moreover, a calculation taking into account the droplets size distribution and the number of nuclei is introduced to explain the crystallization behavior of three different blend ratios.© 1998 John Wiley & Sons, Inc. J. Polym. Sci. B Polym. Phys. 36: 2573-2585, 1998
Additional Material:
9 Ill.
Type of Medium:
Electronic Resource