Abstract Specimens of a stainless steel (20%Cr, 25%Ni stabilized with niobium and also containing 0.9% Mn and 0.6% Si) implanted with lanthanum to a dose of 1017 ion cm−2 , together with unimplanted specimens, have been oxidized in carbon dioxide at 825° C for times up to 9735 h. Transverse sections through the oxide scales formed on the respective specimens have been studied by analytical electron microscopy. After this exposure the scale on the unimplanted 20/25/Nb stainless steel consists of an outer, large-grained, spinel layer, a middle fine-grained Cr2O3 layer and an inner, discontinuous silicon rich, niobium and chromium bearing, amorphous layer. The main effects of the lanthanum implantation are to improve oxidation resistance and maintain scale adherence during thermal cycling. The microstructural changes in the scale formed on the lanthanum implanted 20/25/Nb steel include finer Cr2O3 oxide grains and an intermediate region between the outer spinel and inner Cr2O3 layers comprised of both oxides. The lanthanum concentrates in this region and appears to act as a marker due to its low diffusivity. Mechanisms of scale development on the 20/25/Nb stainless Red and the influence of lanthanum implantation are discussed.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1007/BF01160752