Description / Table of Contents:
Field corrosion tests on hot dip galvanized steel pipes - Assessment of long term dataThe degree of metal loss and its time dependence of hot dip galvanized steel pipes in flowing waters were correlated with the water parameters. A good correlation was observed with CO2 concentration of the water. The higher the initial corrosion rate the higher is in many cases the decrease in corrosion rate with time. This is explained in terms of increased iron oxide content in the protective layers formed after the dissolution of a significant amount of zinc layer. Except phosphates the other water parameters (chlorides, sulphates, nitrates and TOC) do not exhibit any influence. The favourable influence of the iron oxide rich protective layers on the corrosion rate may get lost in waters very rich in carbon dioxide.
Notes:
Die Zeitabhängigkeit und die Höhe der Massenverluste von feuerverzinkten Stahlrohren in fließenden Wässern wurde mit Wasserparametern verglichen. Es zeigte sich eine gute Korrelation mit der Kohlensäurekonzentration. Die Korrosionsgeschwindigkeiten nehmen im allgemeinen mit der Zeit um so stärker ab, je größer die anfänglichen Korrosionsabträge sind. Dies wird auf den Einbau von Eisenoxid in den Deckschichten nach weitgehender Korrosion der Verzinkung gedeutet. Ein zusätzlicher Einfluß von Wasserparametern (Chloride und Sulfate, Nitrate, org. C) wurde mit Ausnahme von Phosphat nicht beobachtet. In sehr kohlensäurereichen Wässern entstehen keine schützenden eisenoxidreichen Deckschichten.
Additional Material:
1 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19870380504